The effects of Nd3+ concentration on the visible fluorescence spectroscopic properties of Nd:(Y0.9La0.1)2O3 transparent ceramics are investigated. Under 270 nm excitation, three emission peaks are observed at 396, 426, and 633 nm. When the Nd3+ concentration is increased, intensities of the peaks at 396 and 426 nm increase while the 633 nm peak become weak due to the fluorescence re-absorption effect. Broad luminescence band centered at 426 nm is observed from the fluorescence spectrum stimulated at 358 nm. The emission intensity increases with the increase of Nd3+ ion content firstly, then decreases owing to the concentration quenching of Nd3+ ions.
160.5690 Rare-earth-doped materials 300.6280 Spectroscopy, fluorescence and luminescence 160.4670 Optical materials Chinese Optics Letters
2012, 10(s2): S21604